Pearlized PP

Composition

Biaxially oriented polypropylene film + transparent coating used as label facestock

● High glossy, pearlized finishing, good smooth

● Good stiffness, tearproof ,resistance of water and humidity,environmentally friendly

● Excellent printing performance. compatible with most conventional printing,such as flexography, screen, letterpress

● Compatible with cold stamping

Test		Norm	Unit	40um	60um	70um
Width Tolarance		GB/T6673	mm	±2	±2	±2
Apperance		Visual Inspection	-	No wrinkle, no scratch, no obvious defect on surface
Thickness Tolarance	Max/Min	GB/T6672	um	40±4	62±4	70±4
Thickness Tolarance	Average	GB/T6672	um	40±3	62±3	70±3
Product Weight/sqm		Electronic Balance	g	36±3	45±3	54±3
Coating Weight/sqm		Electronic Balance	g	3-5	3-5	3-5
Surface Tension		GB/T14216	Dyn/cm	≥40	≥40	≥40
Coating Fastness		3M810	Grade	≥4	≥4	≥4
Whiteness		GB7974	%	75±5	75±3	80±5
Gloss(60°)		ISO2813 60°	Gs	45±5	55±5	45±5
Tensile Strength	MD	GB/T1040	Mpa	≥40	≥80	≥40
Tensile Strength	CD	GB/T1040	Mpa	≥100	≥150	≥100
Enlongation	MD	GB/T1040	%	≤200	≤250	≤200
Enlongation	CD	GB/T1040	%	≤100	≤100	≤100
Shrinkage	MD	120℃/5min	%	≤5	≤3	≤5
Shrinkage	CD	120℃/5min	%	≤3	≤2	≤3

Standard Thickness: 40um/60um/70um

Suitable for printing: flexography, letterpress, screen printing, offset, etc.

Recommend storage conditions: T 25℃ , Humidity 65%

● Used as PS label facestock with high glossy and pearlized finishing

● Mainly for daily-use and food product labels