Fast Dry Synthetic PP Paper

Composition

Biaxially oriented polypropylene film + fast dry matte white coating used as label facestock

● High value of whiteness, excellent fine and smooth coating

● Good stiffness, tearproof ,resistance of water and humidity,environmentally friendly

● Excellent printing performance. compatible with most conventional printing,such as flexography, offset, screen, letterpress

● Fast dry for printing

● High product yield rate for lamination

Test		Norm	Unit	54um	75um	95um
Width Tolarance		GB/T6673	mm	±2	±2	±2
Apperance		Visual Inspection	-	No wrinkle, no scratch, no obvious defect on surface
Thickness Tolarance	Max/Min	GB/T6672	um	54±4	74±4	94±4
Thickness Tolarance	Average	GB/T6672	um	54±3	74±3	94±3
Product Weight/sqm		Electronic Balance	g	45±4	58±4	74±4
Coating Weight/sqm		Electronic Balance	g	7-9	7-9	7-9
Surface Tension		GB/T14216	Dyn/cm	≥40	≥40	≥40
Coating Fastness		3M810	Grade	≥4	≥4	≥4
Whiteness		GB7974	%	78±5	90±5	90±5
Gloss(60°)		ISO2813 60°	Gs	3-8	3-8	3-8
Opacity		ISO2471-77	%	83±3	90±3	92±3
Tensile Strength	MD	GB/T1040	Mpa	≥40	≥40	≥40
Tensile Strength	CD	GB/T1040	Mpa	≥70	≥100	≥100
Enlongation	MD	GB/T1040	%	≤200	≤200	≤200
Enlongation	CD	GB/T1040	%	≤100	≤100	≤100
Shrinkage	MD	120℃/5min	%	≤5	≤5	≤5
Shrinkage	CD	120℃/5min	%	≤3	≤3	≤3

Standard Thickness: 54um/75um/95um

Suitable for printing: flexography, letterpress,screen printing, offset, etc.

Recommend storage conditions: T 25℃ , Humidity 65%

Used as PS label facestock for wide applications